Siliceous frustules were extracted from a representative fresh water diatom species (Cyclotella sp.) by treating with aqueous hydrochloric (HCl) acid. The structural characterizations of cleaned frustules were examined by scanning electron microscope (SEM). The microscopy images showed that the diatoms have a regular circular shape and are of almost equal size (average length is 9 m and average width is 3 m).It was observed that the frustules were composed mostly of silica ( 87 at %), and metal oxides ( 11.5 at %) as found ...
Read More
Siliceous frustules were extracted from a representative fresh water diatom species (Cyclotella sp.) by treating with aqueous hydrochloric (HCl) acid. The structural characterizations of cleaned frustules were examined by scanning electron microscope (SEM). The microscopy images showed that the diatoms have a regular circular shape and are of almost equal size (average length is 9 m and average width is 3 m).It was observed that the frustules were composed mostly of silica ( 87 at %), and metal oxides ( 11.5 at %) as found from FT-IR and EDX measurements. Optical emission showed clear bands at 440 and 375 nm which arise due to silica microstructures of size 200 nm. Photonics device can be manufactured with this nature made nanostructure.
Read Less
Add this copy of Nano-structured silica on diatoms and its optical to cart. $22.17, new condition, Sold by Ingram Customer Returns Center rated 5.0 out of 5 stars, ships from NV, USA, published 2015 by LAP Lambert Academic Publishing.
Add this copy of Nano-structured silica on diatoms and its optical to cart. $39.23, new condition, Sold by Ria Christie Books rated 5.0 out of 5 stars, ships from Uxbridge, MIDDLESEX, UNITED KINGDOM, published 2015 by LAP Lambert Academic Publishing.